全商网(guihenongye.com)以下是全商网PC为大家提供的供应PC日本出光IRY2200 低粘度 防火级的信息,希望对您有所帮助!
PC日本出光IRY2200 低粘度 防火级
电气性能 | 绝缘破坏电压 | --- | --- | 30 | kv/mm |
体积固有电阻 | --- | --- | <1016 | Ω.m | |
电容率 | 60Hz | --- | 2.91 | --- | |
电容率 | 1MHz | --- | 2.85 | --- | |
介质衰耗因数 | 60Hz | --- | 6.6×10-4 | --- | |
介质衰耗因数 | 1MHz | --- | 9.2×10-4 | --- | |
耐电弧性 | --- | --- | 110 | sec | |
加工性能 | 成型收缩率 | --- | --- | 0.5~0.7% | % |
热 性 能 | 线膨胀系数 | --- | --- | 6.5 | ×10-5cm/cm/℃ |
燃烧性 | 3mm | --- | V-0 | --- | |
载荷挠曲温度 | --- | --- | 148 | ℃ | |
维卡软化点 | --- | --- | 148 | ℃ |
基本性能 | 吸水率 | --- | --- | 0.23 | % |
熔体流动速率 | --- | --- | 12 | g/10min | |
物理性能 | 光线透射率 | --- | --- | 85~89 | % |
比重 | --- | --- | 1.20 | --- | |
机械性能 | 伸张屈服强度 | --- | --- | 64 | MPa |
伸张抗断强度 | --- | --- | 68 | MPa | |
伸张弹性模量 | --- | --- | 2300 | MPa | |
破坏伸张率 | --- | --- | 115 | % | |
抗挠强度 | --- | --- | 93 | MPa | |
弯曲弹性模量 | --- | --- | 2350 | MPa | |
IZOD冲击强度 | 4mm | --- | 70 | KJ/m2 | |
IZOD冲击强度 | 3.2mm | --- | 90 | KJ/m2 | |
罗氏硬度 | --- | --- | R120(M75) | --- | |
滑动摩擦 | --- | --- | 12 | --- |
1) 料筒温度。料筒温度对塑件质量影响很大,料温低时会造成缺料,表面无光泽及银丝;料温高时易产生溢料,出现气泡及变色。一般料筒温度控制在230~310℃。对于薄壁制品,料筒温度应取大值;对厚壁制品可取小值。
2) 模具温度。一般情况下,塑件中的内应力与冷却时的模温和料温的差值大致成正比关系,因此要求模温较高,模温可控制在80—120℃,薄壁塑件宜取80~100C,厚壁塑件宜取100~120℃。若模温超过120℃,塑件冷却慢,易粘模,脱模困难,容易翘曲,成型周期较长。
3) 注射压力。PC熔体的粘度较高,因此需要较大的成型压力。使用螺杆式注塑机时,注射压力一般为70~140MPa,而柱塞式注塑机为100~160MPa。可根据原料、塑件、模具及注塑机的不同情况而定。
上面就是PC为大家带来的:供应PC日本出光IRY2200 低粘度 防火级的全部内容了,更多的相关信息请关注PC分类。