厂家直销PPS R10-7006A 玻纤矿物增强
| 机械性能 | 抗拉强度 | --- | ASTM D-638 | 22.0 | Ksi | ||||||||
| 伸长率 | --- | ASTM D-638 | 1.2 | % | |||||||||
| 抗折强度 | --- | ASTM D-790 | 29.5 | Ksi | |||||||||
| 抗拉模数 | --- | ASTM D-790 | 2.1 | Msi | |||||||||
| 抗压强度 | --- | ASTM D-695 | 26.0 | Ksi | |||||||||
| 弹性模数 | --- | ASTM D-638 | 2.2 | Msi | |||||||||
|
--- |
|
|
|
|||||||||
| 电气性能 | 绝缘破坏电压 | --- | ASTM D-149 | 450 | V/mil | ||||||||
| 介电质常数 | 1KHz | ASTM D-150 | 3.9 | --- | |||||||||
| 介电常质数 | 1MHz | ASTM D-149 | 3.8 | --- | |||||||||
| 捐耗因素 | 1KHz | ASTM D-150 | 0.002 | --- | |||||||||
| 损耗因素 | 1MHz | ASTM D-150 | 0.0014 | --- | |||||||||
| 体积电阻率 | --- | ASTM D-257 | 1×1016 | Ω.cm | |||||||||
| 耐电弧 | --- | ASTM D-495 | 125 | Sec | |||||||||
| 电弧踪迹 | --- | UL 746A | 7.1 | in/min | |||||||||
| CTI踪迹 | --- | UL 746A | 7.1 | V | |||||||||
| 绝缘电阻 | --- | --- | 1×1011 | Ω | |||||||||
| 热 性 能 | UL温度指数 | --- | UL | 200/220 | °C | ||||||||
| 燃烧性 | --- | UL 94 | V-0/5VA | --- | |||||||||
| 热变形温度 | 264psi | ASTM D-648 | >500 |
1.干燥
建议的干燥温度为150-160°C，为期2-3小时。若使用热风干燥机，置于盘中之原料高度不应高于50mm。若使用除湿干燥机，其入口温度为-40°C露点。
2.注塑速度
注塑速度不同，产品的表面光这度就不一样，速度越快，表面光泽越好，但容易发生产品翘曲，烧焦，对此必须注意。一般使用中等速度，较高注射压力条件成型。
由于PPS树脂是结晶性树脂，在厚壁成型时，通常为提高结晶度，必须拉长冷却时间，而在薄壁成型时，即使一次成型个数很多，每一循环10-30秒就已足够。
成型时的螺杆转速一般为40-100RPM，而高循环成型时虽可采用200RPM以上，但此时树脂易发热，必须将机筒温度设定较低些。